Posted: Fri Sep 29, 2017 4:33 pm Post subject: Red-rot--at what point does it matter? |
|
|
There are visible spots of red-rot on the lead pipe of my 1970s Severinsen Getzen trumpet. I don't care about cosmetics.
I think of red-rot as a kind of cancer that rots metal away. Eventually, the holes will rot all the way through and air will escape.
But, until that happens do I need to worry about it? Before it rots all the way through, will it cause problems with the way the air circulates that will make the horn sound, resonate or respond differently?
And when it finally goes all the way through and cause air leaks, can't I just get a patch to seal the air in? |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
yourbrass Heavyweight Member
Joined: 12 Jun 2011 Posts: 3636 Location: Pacifica, CA, USA
|
Posted: Fri Sep 29, 2017 5:35 pm Post subject: |
|
|
It won't cause any problems until it gets so widespread that the pipe starts cracking open. In 99% of horns I've seen, it doesn't affect it much. You can have it acid-cleaned, which gets some of the moss out of the inside, but it isn't necessary. And that's a replaceable part, so no big deal.
-Lionel _________________ "Strive for tone." -John Coppola
Edwards X-13
ACB MV3C /ACB A1/26 backbore
https://yourbrass.com/ |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
Brad361 Heavyweight Member
Joined: 16 Dec 2007 Posts: 7080 Location: Houston, TX.
|
Posted: Sat Sep 30, 2017 7:57 am Post subject: |
|
|
yourbrass wrote: | It won't cause any problems until it gets so widespread that the pipe starts cracking open. In 99% of horns I've seen, it doesn't affect it much. You can have it acid-cleaned, which gets some of the moss out of the inside, but it isn't necessary. And that's a replaceable part, so no big deal.
-Lionel |
I agree, and I definitely take what someone who actually IS a tech as correct.
But personally, being obsessive compulsive, even though I know red rot takes a long time to get to a point where you need to replace a leadpipe, it would still drive me nuts if it was in a horn I liked.
As said, that’s just OCD-me.
Brad _________________ When asked if he always sounds great:
"I always try, but not always, because the horn is merciless, unpredictable and traitorous." - Arturo Sandoval |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
Dieter Z Veteran Member
![](images/avatars/1427725485862b97693c1b.jpg)
Joined: 21 Jun 2013 Posts: 449 Location: Mountains of North Carolina
|
Posted: Sat Sep 30, 2017 8:02 am Post subject: |
|
|
Relax!!! _________________ B & H Sovereign 928
Conn 80A
F. Besson Brevette Kanstul made
B&S Challenger II 3137 rl
Buescher 400 - 225 (WWII)
Benge 90C
Eastman 540 D/Eb
ACB Fluegelhorn
Selmer Picc
ACB mouthpieces for most of my playing |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
shofarguy Heavyweight Member
Joined: 18 Sep 2007 Posts: 7013 Location: AZ
|
Posted: Sat Sep 30, 2017 8:47 am Post subject: |
|
|
I asked this question in one conversation with Byron Autrey. My Benge was showing a little dark area inside the lead pipe. He said pretty much what "your brass" said, with the addition that, as the pitting got worse, the horn might lose some of its focus and slotting. He recommended I clean the inside of the lead pipe with ultra fine (1500 grit) sandpaper rather than change out the pipe, since the rot hadn't progressed very far. That was Zig Kanstul's assessment, as well. They felt was a bigger risk because I might not like how the horn played after the change of pipe. _________________ Brian A. Douglas
Flip Oakes Wild Thing Bb Trumpet in copper
Flip Oakes Wild Thing Flugelhorn in copper
There is one reason that I practice: to be ready at the downbeat when the final trumpet sounds. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
markp Heavyweight Member
Joined: 15 Feb 2005 Posts: 2814 Location: Coarsegold, CA
|
Posted: Sat Sep 30, 2017 10:37 am Post subject: |
|
|
shofarguy wrote: | I asked this question in one conversation with Byron Autrey. My Benge was showing a little dark area inside the lead pipe. He said pretty much what "your brass" said, with the addition that, as the pitting got worse, the horn might lose some of its focus and slotting. He recommended I clean the inside of the lead pipe with ultra fine (1500 grit) sandpaper rather than change out the pipe, since the rot hadn't progressed very far. That was Zig Kanstul's assessment, as well. They felt was a bigger risk because I might not like how the horn played after the change of pipe. |
THIS is what I'm worried about--the horn losing focus and slotting, and then not being the same with a replacement pipe. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
John Mohan Heavyweight Member
![](images/avatars/10803205995eed11f66eacb.jpg)
Joined: 13 Nov 2001 Posts: 9830 Location: Chicago, Illinois
|
Posted: Sat Sep 30, 2017 10:41 am Post subject: |
|
|
It's important to note that "red rot" is not really like cancer in so far as removing the existing oxidation does not inhibit future oxidation the way removing cancerous tissue stops further cancer growth (if you get it all). In fact, with some metals (including aluminum), it is the fact that the metal oxidizes quickly and forms a thin layer of oxidized metal that stops the oxidation process, that makes such metals less prone to (deep) corrosion.
While removing the oxidation from the inside of a leadpipe is a good idea, to prevent continued oxidation, just squirt some valve oil into the leadpipe every few days to keep the inside of it coated and keep the oxygen away from the metal.
Cheers,
John Mohan
Skype Lessons Available - Click on the e-mail button below if interested _________________ Trumpet Player, Clinician & Teacher
1st Trpt for Cats, Phantom of the Opera, West Side Story, Evita, Hunchback of Notre Dame,
Grease, The Producers, Addams Family, In the Heights, etc.
Ex LA Studio Musician
16 Year Claude Gordon Student |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
halfgreek12 Veteran Member
Joined: 21 Aug 2008 Posts: 201 Location: Albany, NY
|
Posted: Sat Sep 30, 2017 10:43 am Post subject: |
|
|
I've had good luck using gun bore hones on a drill to clean out old lead pipes. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
yourbrass Heavyweight Member
Joined: 12 Jun 2011 Posts: 3636 Location: Pacifica, CA, USA
|
Posted: Sat Sep 30, 2017 11:17 am Post subject: |
|
|
I wouldn't recommend sandpaper, hones, or anything that cuts or abrades. My method is to plug the tuning slide end of the pipe, fill with muriatic acid, and let set for a couple of minutes. Then rinse, scrub out, and soak the pipe in a soapy water/baking soda bath for another couple of minutes. Inside of the pipe often comes out looking brand new.
HOWEVER, I don't recommend trying this at home, this is for someone used to the correct practice and timing of the procedure to do it. And, sometimes the zinc leaching will continue and show up in the pipe after a short time. Depends on the alloy, how far the dezincification has gone, etc.
John's recommendation of valve oil down the pipe every day is an excellent one; it sets up a barrier that slows down the effects of your body's acids on the metal. Keep it clean and oiled!
-Lionel _________________ "Strive for tone." -John Coppola
Edwards X-13
ACB MV3C /ACB A1/26 backbore
https://yourbrass.com/ |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
ghelbig Heavyweight Member
![](images/avatars/200969850357fbe1af8cf46.jpg)
Joined: 27 May 2011 Posts: 908 Location: Reno, NV
|
Posted: Sat Sep 30, 2017 12:01 pm Post subject: |
|
|
John Mohan wrote: | While removing the oxidation from the inside of a leadpipe is a good idea, to prevent continued oxidation, just squirt some valve oil into the leadpipe every few days to keep the inside of it coated and keep the oxygen away from the metal. |
Red-rot isn't oxidation (oxidized brass is green), but I can't argue with the advice.
wiseGEEK wrote: | Dezincification of brass is a form of selective corrosion that happens when zinc is leached out of the alloy leaving a weakened porous copper fitting. This commonly happens in chlorinated water or in water that has high levels of oxygen and carbon dioxide. |
www.wisegeek.com/what-is-dezincification.htm
Gary. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
LittleRusty Heavyweight Member
Joined: 11 Aug 2004 Posts: 12664 Location: Gardena, Ca
|
Posted: Sat Sep 30, 2017 12:15 pm Post subject: |
|
|
There was a product that a couple of our members tried to bring to market that would coat the surfaces and prevent red-rot. But unfortunately it didn't make it.
As to using valve oil down the leadpipe, since it will coat the same surfaces that the water accumulates in the instrument it probably is effective enough. But to be really effective one should ensure all of the surfaces are coated. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
adagiotrumpet Heavyweight Member
Joined: 31 May 2006 Posts: 906
|
Posted: Sat Sep 30, 2017 12:41 pm Post subject: |
|
|
I bought an old horn that was not well taken care of. No amount of soaking and scrubbing would loosen the corrosion inside the lead pipe. I even sent it in for a chemical cleaning, but although that helped, it did not remove all of the corrosion inside the lead pipe. It was recommended that I try muriatic acid, but having not used it before, I was reluctant to try it. I did however go to a hardware store and buy rubber stoppers that fit the lead pipe. I then put the horn on a trumpet stand, put a stopper in the lower end of the lead pipe and filled the lead pipe with white vinegar. I left it in there for a few minutes, drained it and scrubbed it with a stiff nylon brush. A construction supply house that sells epoxy anchors will have stiff, round nylon brushes of various diameters with long handles. After scrubbing the lead pipe, much of the corrosion was removed. Not wanting to leave the vinegar in too long since it is an acid, I repeated the process several more times finally removing practically all of the corrosion. I then filled the lead pipe with baking soda and water to neutralize the vinegar and then rinsed it with a lot of clean water.
I would be interested in any repairmen commenting on the wisdom of this procedure. Just because it worked for me doesn't mean it was necessarily a good idea. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
Hugh Anderson Veteran Member
Joined: 22 Sep 2011 Posts: 398
|
Posted: Sat Sep 30, 2017 2:48 pm Post subject: |
|
|
1500 grit sandpaper is similar to brown sack paper. 2000 more accurately. It won't hurt much. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
shofarguy Heavyweight Member
Joined: 18 Sep 2007 Posts: 7013 Location: AZ
|
Posted: Sat Sep 30, 2017 2:49 pm Post subject: |
|
|
LittleRusty wrote: | There was a product that a couple of our members tried to bring to market that would coat the surfaces and prevent red-rot. But unfortunately it didn't make it.
As to using valve oil down the leadpipe, since it will coat the same surfaces that the water accumulates in the instrument it probably is effective enough. But to be really effective one should ensure all of the surfaces are coated. |
The product was called STOP Rot! It worked very well. nPart was the company that designed the applicator and found the proper preparation for the nano-coating. The coating was an exotic polymer suspended in floruosolvent, which is used in surgeries and leaves no residue. The polymer bound itself to the brass in a one molecule layer and blocked large molecules from attacking the zinc.
We could not guarantee the product would eliminate the formation of red rot, because rot is often formed at the foundry and present when the instrument is manufactured. Our product was self-applied by the purchaser, which was a second reason we could not guarantee its performance.
One particular poster went over the top to discredit our efforts and accused us of peddling a product that would kill people. Yes, he did. The group of posters that joined in on this line of thinking cursed our single molecule layer, of what is essentially a plastic, as somehow far more dangerous than breathing the fumes of valve oil (which is thousands of molecules thicker and made of known carcinogenic petroleum elements) sent down the lead pipe.
I still have hundreds of applicators and more product packages in storage. The shelf life is not known, so I cannot confidently stand behind those units. I did coat my flugelhorn with the nano coating and it did just we said it would do. _________________ Brian A. Douglas
Flip Oakes Wild Thing Bb Trumpet in copper
Flip Oakes Wild Thing Flugelhorn in copper
There is one reason that I practice: to be ready at the downbeat when the final trumpet sounds. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
RL Veteran Member
Joined: 06 Sep 2009 Posts: 162
|
Posted: Sun Oct 01, 2017 3:54 am Post subject: |
|
|
It will take a while (had the same with an older Getzen cornet which I bought second hand - including red rot as a bonus) sold it after years and it was still in the same condition as I bought it. Maybe Getzen still has leadpipes in stock?
You can ask them..They've a great customerservice... |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
yourbrass Heavyweight Member
Joined: 12 Jun 2011 Posts: 3636 Location: Pacifica, CA, USA
|
Posted: Tue Oct 03, 2017 7:21 am Post subject: |
|
|
adagiotrumpet wrote: | I bought an old horn that was not well taken care of. No amount of soaking and scrubbing would loosen the corrosion inside the lead pipe. I even sent it in for a chemical cleaning, but although that helped, it did not remove all of the corrosion inside the lead pipe. It was recommended that I try muriatic acid, but having not used it before, I was reluctant to try it. I did however go to a hardware store and buy rubber stoppers that fit the lead pipe. I then put the horn on a trumpet stand, put a stopper in the lower end of the lead pipe and filled the lead pipe with white vinegar. I left it in there for a few minutes, drained it and scrubbed it with a stiff nylon brush. A construction supply house that sells epoxy anchors will have stiff, round nylon brushes of various diameters with long handles. After scrubbing the lead pipe, much of the corrosion was removed. Not wanting to leave the vinegar in too long since it is an acid, I repeated the process several more times finally removing practically all of the corrosion. I then filled the lead pipe with baking soda and water to neutralize the vinegar and then rinsed it with a lot of clean water.
I would be interested in any repairmen commenting on the wisdom of this procedure. Just because it worked for me doesn't mean it was necessarily a good idea. |
Essentially, that's what I do in the shop, but using muriatic (hydrochloric) acid instead of vinegar. The risks of muriatic to the uninitiated include skin burns, really black marks if spilled on silver plating, and assorted other consequences. You should see how it screws up the finish on stainless steel. Or maybe you shouldn't.
Dezincification is such a slow process that it really is a good idea to have a pro do the cleaning, then it's easy for the player to keep clean without the need for any acid. _________________ "Strive for tone." -John Coppola
Edwards X-13
ACB MV3C /ACB A1/26 backbore
https://yourbrass.com/ |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
lipshurt Heavyweight Member
Joined: 24 Feb 2008 Posts: 2642 Location: vista ca
|
Posted: Tue Oct 03, 2017 9:24 am Post subject: |
|
|
I will say that even a little red rot makes a negative impact on a horn.
I have a box full of bach, martin, olds, calichio, yamaha, conn 22b, and other pipes. About maybe 50 pipes. They are all pipes that i took off people horns when they wanted to try a different pipe. Usually they would give me the old pipe that did not like. About every one of them has some amount of red rot. some only a little.
I have several, like 10 or 15 bach pipes that have only a tiny bit of rot that you can see when looking inside the pipe. NONE of these have anything close to rot showing on the outside. Every time i try to use one of them, those pipes just are not as good as a perfectly clean shiny pipe. Its a big dif. You can polish the inside of the pipe and get the rot pretty smooth, and its better. But I can feel when its not perfect. Response, and core of the sound are affected the most. Playing soft, and keeping ping and core is tough with any amount of see-able rot. _________________ Mouthpiece Maker
vintage Trumpet design enthusiast
www.meeuwsenmouthpieces.com
www.youtube.com/lipshurt |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
shofarguy Heavyweight Member
Joined: 18 Sep 2007 Posts: 7013 Location: AZ
|
Posted: Tue Oct 03, 2017 11:01 am Post subject: |
|
|
lipshurt wrote: | I will say that even a little red rot makes a negative impact on a horn.
I have a box full of bach, martin, olds, calichio, yamaha, conn 22b, and other pipes. About maybe 50 pipes. They are all pipes that i took off people horns when they wanted to try a different pipe. Usually they would give me the old pipe that did not like. About every one of them has some amount of red rot. some only a little.
I have several, like 10 or 15 bach pipes that have only a tiny bit of rot that you can see when looking inside the pipe. NONE of these have anything close to rot showing on the outside. Every time i try to use one of them, those pipes just are not as good as a perfectly clean shiny pipe. Its a big dif. You can polish the inside of the pipe and get the rot pretty smooth, and its better. But I can feel when its not perfect. Response, and core of the sound are affected the most. Playing soft, and keeping ping and core is tough with any amount of see-able rot. |
Interesting. _________________ Brian A. Douglas
Flip Oakes Wild Thing Bb Trumpet in copper
Flip Oakes Wild Thing Flugelhorn in copper
There is one reason that I practice: to be ready at the downbeat when the final trumpet sounds. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
Glissando Veteran Member
![](images/avatars/7529163484f78b3b114ca5.png)
Joined: 28 Apr 2007 Posts: 245
|
Posted: Tue Oct 03, 2017 2:20 pm Post subject: |
|
|
Does anybody have any actual information (proof) that putting valve oil down the lead pipe actually helps prevent red rot?
Hoping for actual information here, not just opinions that don't have a strong basis.
I ask because I, too, have oiled the lead pipe for years -- but water and oil don't mix, so I always wonder whether there's really much coating of the brass going on. Even if you add the oil before playing (when there should be less moisture, presumably providing more dry brass for the oil to adhere to), it seems a lot to expect a few randomly dripped drops of oil to coat everything very well.
And then even if you do get some coating to begin with, one imagines that the oil would get diluted as you play -- adding moisture from your breath, draining the system with the water key, and repeating the process again and again. Seems like the drops of oil would be progressively diluted, and much of those few drops of oil would quickly go out the spit valve. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
shofarguy Heavyweight Member
Joined: 18 Sep 2007 Posts: 7013 Location: AZ
|
Posted: Tue Oct 03, 2017 2:40 pm Post subject: |
|
|
Glissando wrote: | Does anybody have any actual information (proof) that putting valve oil down the lead pipe actually helps prevent red rot?
Hoping for actual information here, not just opinions that don't have a strong basis.
I ask because I, too, have oiled the lead pipe for years -- but water and oil don't mix, so I always wonder whether there's really much coating of the brass going on. Even if you add the oil before playing (when there should be less moisture, presumably providing more dry brass for the oil to adhere to), it seems a lot to expect a few randomly dripped drops of oil to coat everything very well.
And then even if you do get some coating to begin with, one imagines that the oil would get diluted as you play -- adding moisture from your breath, draining the system with the water key, and repeating the process again and again. Seems like the drops of oil would be progressively diluted, and much of those few drops of oil would quickly go out the spit valve. |
It's a good question, as some oils use alcohols as thinners and paraffin as a lubricant, too. I know that alcohol absorbs water and I think paraffin might a little. If the oil has detergents in it, they act to lower the hydro-phobic qualities of the oil. _________________ Brian A. Douglas
Flip Oakes Wild Thing Bb Trumpet in copper
Flip Oakes Wild Thing Flugelhorn in copper
There is one reason that I practice: to be ready at the downbeat when the final trumpet sounds. |
|
Back to top |
|
![](templates/subSilver/images/spacer.gif) |
|
|
You cannot post new topics in this forum You cannot reply to topics in this forum You cannot edit your posts in this forum You cannot delete your posts in this forum You cannot vote in polls in this forum
|
Powered by phpBB © 2001, 2005 phpBB Group
|